Section Code 5365 : Ethylene Propylene Diene Monomer (EPDM) - material only. Components made from materials listed in this section may be required to be submitted for audit tests.
Back To Directory Sections'DLYY E6202'. Black coloured, compression moulded EPDM material. Shore hardness 60. Tested in-radius size 1.0mm. For use with water up to 23°C.
EP0E7001P-WRC. Black coloured, compression moulded EPDM sheet material. Shore hardness 70. Tested in-radius size 1.1mm. For use with water up to 85°C.
'E7131'. Black coloured, injection moulded EPDM rubber material. Shore hardness 70. Tested in-radius size 1.0mm. For use with water up to 85°C.
'E7008W'. Black coloured, compression moulded EPDM material. Shore hardness 70. Tested in-radius size 1.05mm. For use with water up to 85°C.
'EPDM PX Black SH 78'. Black coloured, injection moulded EPDM material. Shore hardness 78. Tested in-radius size 1.0mm. For use with water up to 85°C.
‘EPDM-FF’. Black coloured, compression moulded EPDM rubber material. Shore hardness 80A. Tested in-radius size 0.89mm. For use with water up to 85°C.
'TIMO-70'. Black coloured, injection moulded EPDM rubber material. Shore hardness 70. Tested in-radius size 1.17mm. For use with water up to 85°C.
'H600071'. Black coloured, compression moulded EPDM material. Shore hardness 55. Tested in-radius size 1.25mm. For use with water up to 65°C.
'51M6767'. Black coloured, injection moulded EPDM material. Shore hardness 67. Tested in-radius size 0.5mm. For use with water up to 60°C.
'TWK3628'. Black coloured, injection moulded EPDM material. Shore hardness 67. Tested in-radius size 0.5mm. For use with water up to 60°C.
Page 2 of 19
We use cookies to give you the best possible experience with WRAS. Some are essential to provide website functions and ensure the website is secure. We also use cookies to help us understand how people use the site and to make improvements. Click "Accept All" to enable recommended settings or click "Manage cookies" to adjust your settings. For more details, see our Cookie Policy.